The boundary lubrication of chemically grafted and cross-linked hyaluronic acid in phosphate buffered saline and lipid solutions measured by the surface forces apparatus

High molecular weight hyaluronic acid (HA) is present in articular joints and synovial fluid at high concentrations; yet despite numerous studies, the role of HA in joint lubrication is still not clear. Free HA in solution does not appear to be a good lubricant, being negatively charged and therefore repelled from most biological, including cartilage, surfaces. Recent enzymatic experiments suggested that mechanically or physically (rather than chemically) trapped HA could function as an “adaptive” or “emergency” boundary lubricant to eliminate wear damage in shearing cartilage surfaces. In this work, HA was chemically grafted to a layer of self-assembled amino-propyl-triethoxy-silane (APTES) on mica and then cross-linked. The boundary lubrication behavior of APTES and of chemically grafted and cross-linked HA in both electrolyte and lipid 1,2-dioleoyl-sn-glycero-3-phosphocholine (DOPC) solutions was tested with a surface forces apparatus (SFA). Despite the high coefficient of friction (COF) of μ ≈ 0.50, the chemically grafted HA gel significantly improved the lubrication behavior of HA, particularly the wear resistance, in comparison to free HA. Adding more DOPC lipid to the solution did not improve the lubrication of the chemically grafted and cross-linked HA layer. Damage of the underlying mica surface became visible at higher loads (pressure >2 MPa) after prolonged sliding times. It has generally been assumed that damage caused by or during sliding, also known as “abrasive friction”, which is the main biomedical/clinical/morphological manifestation of arthritis, is due to a high friction force and, therefore, a large COF, and that to prevent surface damage or wear (abrasion) one should therefore aim to reduce the COF, which has been the traditional focus of basic research in biolubrication, particularly in cartilage and joint lubrication. Here we combine our results with previous ones on grafted and cross-linked HA on lipid bilayers, and lubricin-mediated lubrication, and conclude that for cartilage surfaces, a high COF can be associated with good wear protection, while a low COF can have poor wear resistance. Both of these properties depend on how the lubricating molecules are attached to and organized at the surfaces, as well as the structure and mechanical, viscoelastic, elastic, and physical properties of the surfaces, but the two phenomena are not directly or simply related. We also conclude that to provide both the low COF and good wear protection of joints under physiological conditions, some or all of the four major components of joints—HA, lubricin, lipids, and the cartilage fibrils—must act synergistically in ways (physisorbed, chemisorbed, grafted and/or cross-linked) that are still to be determined.

Adsorption, lubrication, and wear of lubricin on model surfaces : polymer brush-like behavior of a glycoprotein

Using a surface force apparatus, we have measured the normal and friction forces between layers of the human glycoprotein lubricin, the major boundary lubricant in articular joints, adsorbed from buffered saline solution on various hydrophilic and hydrophobic surfaces: i), negatively charged mica, ii), positively charged poly-lysine and aminothiol, and iii), hydrophobic alkanethiol monolayers. On all these surfaces lubricin forms dense adsorbed layers of thickness 60–100 nm. The normal force between two surfaces is always repulsive and resembles the steric entropic force measured between layers of end-grafted polymer brushes. This is the microscopic mechanism behind the antiadhesive properties showed by lubricin in clinical tests. For pressures up to ∼6 atm, lubricin lubricates hydrophilic surfaces, in particular negatively charged mica (friction coefficient μ = 0.02–0.04), much better than hydrophobic surfaces (μ > 0.3). At higher pressures, the friction coefficient is higher (μ > 0.2) for all surfaces considered and the lubricin layers rearrange under shear. However, the glycoprotein still protects the underlying substrate from damage up to much higher pressures. These results support recent suggestions that boundary lubrication and wear protection in articular joints are due to the presence of a biological polyelectrolyte on the cartilage surfaces.

Adaptive mechanically controlled lubrication mechanism found in articular joints

Articular cartilage is a highly efficacious water-based tribological system that is optimized to provide low friction and wear protection at both low and high loads (pressures) and sliding velocities that must last over a lifetime. Although many different lubrication mechanisms have been proposed, it is becoming increasingly apparent that the tribological performance of cartilage cannot be attributed to a single mechanism acting alone but on the synergistic action of multiple "modes" of lubrication that are adapted to provide optimum lubrication as the normal loads, shear stresses, and rates change. Hyaluronic acid (HA) is abundant in cartilage and synovial fluid and widely thought to play a principal role in joint lubrication although this role remains unclear. HA is also known to complex readily with the glycoprotein lubricin (LUB) to form a cross-linked network that has also been shown to be critical to the wear prevention mechanism of joints. Friction experiments on porcine cartilage using the surface forces apparatus, and enzymatic digestion, reveal an "adaptive" role for an HA-LUB complex whereby, under compression, nominally free HA diffusing out of the cartilage becomes mechanically, i.e., physically, trapped at the interface by the increasingly constricted collagen pore network. The mechanically trapped HA-LUB complex now acts as an effective (chemically bound) "boundary lubricant"-reducing the friction force slightly but, more importantly, eliminating wear damage to the rubbing/shearing surfaces. This paper focuses on the contribution of HA in cartilage lubrication; however, the system as a whole requires both HA and LUB to function optimally under all conditions.

Thermal control of high pressure die casting using computational fluid dynamics

The quality of high pressure die castings is a function of many interdependent parameters. It has been observed that many defects detected in the HPDC castings can be tracked back to poor die temperature distribution in the critical areas. It has therefore been recommended that the development of a technique to directly control the critical features - making them less sensitive to thermal related parameters - be very beneficial to the HPDC industry. From the information obtained from thermal image (processing), computational fluid dynamics has been applied to design the layout of internal cooling system and assign the flow conditions such as flow rate and pressure of the cooling water. it is observed that CFD prediction provides an excellent insight into the thermal balance of the high pressure die casting.

Effect of surface roughness of Ti, Zr, and TiZr on apatite precipitation from simulated body fluid

Some of the critical properties for a successful orthopedic or dental implant material are its biocompatibility and bioactivity. Pure titanium (Ti) and zirconium (Zr) are widely accepted as biocompatible metals, due to their non-toxicity. While the bioactivity of Ti and some Ti alloys has been extensively investigated, there is still insufficient data for Zr and titanium-zirconium (TiZr) alloys. In the present study, the bioactivity, that is, the apatite forming ability on the alkali and heat treated surfaces of Ti, Zr, and TiZr alloy in simulated body fluid (SBF), was studied. In particular, the effect of the surface roughness characteristics on the bioactivity was evaluated for the first time. The results indicate that the pretreated Ti, Zr and TiZr alloy could form apatite coating on their surfaces. It should be noted that the surface roughness also critically affected the bioactivity of these pretreated metallic samples. A surface morphology with an average roughness of approximately 0.6 microm led to the fastest apatite formation on the metal surfaces. This apatite layer on the metal surface is expected to bond to the surrounding bones directly after implantation.

Characterization of high fluid strain micro contractions to study the stress on biological fluids

Microfluidics has the potential to enhance the understanding of the biological fluids under strain, due to the laminar nature of the fluid and the possibility to mimic the real conditions. We present advances on charaterization of a microfluidic platform to study high strain rate flows in the transport of biological fluids. These advances are improvements on the reproduction of a  constant extensional strain rate using micro contractions and development of 3D numerical models. The micro geometries have been fabricated in polydimethyl siloxame (PDMS) using standard soft-lithography techniques with a photolithographically patterned mold. A comparison of some microcontractions with different funnel characteristics is presented. The Micro Particle Image Velocimetry technique has been applied to validate the numerical simulations. We demonstrate the use of microfluidics in the reproduction of a large range of controllable extensional strains that can be used in the study of the effect of flow on biological fluids.